ASTM A734/A734M-12

Standard Specification for Pressure Vessel Plates, Alloy Steel and High-Strength Low-Alloy Steel, Quenched-and-Tempered (Withdrawn 2017)

Fecha:
2017-11-03 /Withdrawn
No replacement
Abstract:

This specification covers quenched and tempered alloy steel and high strength low alloy steel plates for piping components and welded pressure vessels. The steel materials shall be killed and shall conform to the fine austenitic grain size requirement. The steel specimens shall undergo heat analysis and product analysis and shall conform to the required chemical compositions of carbon, manganese, phosphorus, sulfur, silicon, copper, nickel, chromium, molybdenum, aluminum, vanadium, nitrogen, and columbium. Tension tests shall be performed wherein the steel materials shall conform to the required values of yield strength, tensile strength, and elongation.

Scope:

1.1 This specification covers quenched-and-tempered alloy steel and high-strength low-alloy steel plates for piping components and welded pressure vessels.

1.2 Two types are covered, which provide two different chemical compositions with the same tensile requirements. Both types are quenched-and-tempered to enhance mechanical properties.

1.2.1 Type A is an alloy steel intended for use at low ambient temperatures of 80°F [60°C] and higher.

1.2.2 Type B is a high-strength low-alloy steel intended for use at ambient temperatures of 20°F [30°C] and higher.

1.3 The maximum thickness of plates is limited only by the capacity of the chemical composition and heat treatment to meet the specified mechanical property requirements. Individual manufacturers should be consulted on thickness limitations since current industry limitations have not been ascertained to date.

1.4 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.

Keywords:
alloy steel plates; pressure containing parts; pressure vessel steels; steel plates; quenched and tempered; high-strength low-alloy steel