ASTM C651-11

ASTM C651-11

Standard Test Method for Flexural Strength of Manufactured Carbon and Graphite Articles Using Four-Point Loading at Room Temperature

Fecha:
2013-11-13 /Historical
Superseeded by:
Abstract:

This test method details the standard procedures for determining the flexural strength of manufactured carbon and graphite articles using a simple beam in four-point loading at room temperature. The four-point loading fixture shall consist of spherical bearing blocks of hardened steel or its equivalent to ensure that forces applied to the beam are normal only and without eccentricity, and distortion of the loading member is prevented. Judicious use of linkages, rocker bearings, and flexure plates may maintain the parallel direction of loads and reactions. The test specimens shall be prepared to yield a parallelepiped with cross sections that are rectangular, faces that are parallel and flat, and edges that are free from visible flaws and chips.

Significance and Use:

4.1 This test method may be used for material development, quality control, characterization, and design data generation purposes.

4.2 This test method determines the maximum loading on a graphite specimen with simple beam geometry in 4point bending, and it provides a means for the calculation of flexural strength at ambient temperature and environmental conditions.

Scope:

1.1 This test method covers determination of the flexural strength of manufactured carbon and graphite articles using a simple beam in four-point loading at room temperature.

1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Keywords:
carbon; flexural strength; graphite; Carbon; Flexural testing; Graphite; Graphite electrodes; Modulus of rupture (MOR)